In the earlier part of this series(Grades of Ordinary Portland
Contents:
Grades of Cement as per American Standard - ASTM C 150
This standard divides Portland cement into eight different types as follows :
| Type I | For use when the special properties specified for any other type are not required. |
| Type IA | Air-entraining cement for the same uses as Type I, where air-entrainment is desired. |
| Type II | For general use, more especially when moderate sulfate resistance or moderate heat of hydration is desired. |
| Type IIA | Air-entraining cement for the same uses as Type II, where air-entrainment is desired. |
| Type III | For use when high early strength is desired. |
| Type IIIA | Air-entraining cement for the same use as Type III, where air-entrainment is desired. |
| Type IV | For use when a low heat of hydration is desired. |
| Type V | For use when high sulfate resistance is desired. |
Some
Air-entraining cement is a special type of cement where air bubbles are intentionally incorporated in the cement by means of special agents. These air bubbles help in providing space for expansion of minute water droplets in concrete due to freezing and thawing action. This protects the concrete from cracking.
Standard Physical Requirement of Various Cement Types
1. Air content of mortar
Air content of mortar in
The code specifically says that the percentage air content indicated here does not ensure that the desired air content will be obtained in concrete.
Code - ASTM C185: Test method for Air Content of Hydraulic Cement Mortar.
2. Fineness
The code specifies two tests that can be used to check the fineness of cement - Turbidimeter test and Air permeability test. Though the code gives liberty to the testing laboratories to decide the method of testing, it specifies that if the sample fails to meet the requirements of air permeability test, the requirements of turbidimeter test will govern.
The code gives the fineness requirement for these two tests in terms of ‘Average Value’ and ‘Any-one sample’. ‘Average value’ is the average value of five consecutive samples tested from a source. The value of ‘Any-one sample’ indicates
When tested for fineness by Turbidimeter test, the specific surface of cement in terms of ‘average value’ (min) shall be 160 m²/kg and in terms of ‘any-one sample’ (min) shall be 150 m²/kg. This is applicable to all grades of cement except Type III and IIIA. The max. value of
When tested for fineness by Air Permeability, the specific surface of cement in terms of ‘average value’ (min) shall be 280 m²/kg and in terms of ‘any-one sample’ (min) shall be 260 m²/kg. This is applicable to all grades of cement except Type III and IIIA.
The max value of
The code does not specify fineness value for type III and IIIA.
Code - ASTM C115: Test Method for Fineness of Portland Cement by the Turbidimeter.
ASTM C204: Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
3. Soundness
When tested by Autoclave test, unaerated cement shall not have an expansion of more than 0.8
Code - ASTM C151: Test Method for Autoclave Expansion of Hydraulic Cement.
4. Compressive Strength:
The compressive strength requirement of various types of cements as specified by the code is given in the table below.
| Cement Type | Compressive Strength in MPa | |||
| 1 day | 3 days | 7 days | 28 days | |
| Type I | --- | 12 | 19 | --- |
| Type IA | --- | 10 | 16 | --- |
| Type II | --- | 10 | 17 | --- |
| Type IIA | --- | 8 | 14 | --- |
| Type III | 12 | 24 | --- | --- |
| Type IIIA | 10 | 19 | --- | --- |
| Type IV | --- | --- | 7 | 17 |
| Type V | --- | 8 | 15 | 21 |
Code - ASTM C109/109M: Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens).
5. Setting Time
When tested by Vicat apparatus method, the setting time of cement shall conform to the following requirement.
Time of setting shall not be less than 45 mins and shall not be more than 375 mins. The setting time requirement is applicable to all grades of cement.
Code - ASTM C191 : Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle.
Grades of Cement as per European Standard - EN-197-1
This code classifies cement in three basic class - Class 32.5, Class 42.5 and Class 52.5 based on the compressive strength of cement mortar cube at 28 days.
Mechanical Requirement of Various Cement Class
1. Compressive Strength
The compressive strength is categorized as mechanical requirement of cement in this code. Based on early strength of cement, each class is divided into two sub-class indicated by N and R.
The class with ordinary early strength is indicated by N and class with high early strength is indicated by R. The compressive strength requirement as specified by the code is given in table below.
| Cement Class | Compressive Strength (MPa) | |||
| Early Strength | Standard Strength | |||
| 2 days | 7 days | 28 days | ||
| 32.5 N | --- | >/= 16.0 | >/= 32.5 | upto 52.5 |
| 32.5 R | >/= 10.0 | --- | ||
| 42.5 N | >/= 10.0 | --- | >/= 42.5 | upto 62.5 |
| 42.5 R | >/=20.0 | --- | ||
| 52.5 N | >/= 20.0 | --- | >/= 52.5 | --- |
| 52.5 R | >/= 30.0 | --- | ||
Code - EN 196-1 : Methods of testing cement. Determination of strength
Physical Requirement of Various Cement Class
1. Initial Setting Time
When tested by Vicat apparatus method, the setting time of cement shall conform to the following requirement.
| Cement Class | Initial Setting Time(mins) |
| 32.5 | >/= 75 |
| 42.5 | >/= 60 |
| 52.5 | >/= 45 |
Code - EN 196-3: Methods of testing cement. Determination of setting times and soundness
2. Soundness
When tested by ‘Le-Chatelier’ method, unaerated cement shall have an expansion of less than or equal to 10mm. This is applicable to all the cement classes.
Code - EN 196-3: Methods of testing cement. Determination of setting times and soundness
References:
- ASTM C150-07 : Standard Specification for Portland Cement.
- EN 197-1 : Composition, specifications and conformity for common cements.
- https://test.theconstructor.org/concrete/air-entrained-cement/23745/