How can we reduce laitance from concrete structures?
Do you need to remove the ads? Become VIP Member
Join TheConstructor to ask questions, answer questions, write articles, and connect with other people. When you join you get additional benefits.
Log in to TheConstructor to ask questions, answer people’s questions, write articles & connect with other people. When you join you get additional benefits.
Lost your password? Please enter your email address. You will receive a link and will create a new password via email.
How can we reduce laitance from concrete structures?
aviratdhodare
The appearance of cement-sand particle on the surface of freshly places concrete is known as laitance.
Precautions to be taken:
1. Clay, silt, dust content should be removed before mixing the concrete.
2. Maintain W/C ratio.
3. Do not sprinkle water during finishing work of concrete.
4. Use well graded F.A. in mix.
5. Use water-reducing admixture little in concrete mix
vivek gami
reason of laitance in concrete.
preventive steps are as follow-–
Preet Chovatiya
Laitance can be avoided by reducing or controlling water during the mixture of concrete. It too much water exists, then other issues also be happening like greater shrinkage and the possibility of more cracks in the structure.
If you want to remove laitance, then It is very easy to remove by acid etchings solution.
Kuldeep Singh
Laitance arises in concrete primarily due to excessive water, improper mixing, curing, batching, and from improper finishing. Also, too much cement or fine sand helps to cause laitance.
So, to prevent laitance :
Vivek Patel
When cement slurry come out on surface that’s call laitance. It is prevented by following steps
Vivek Patel
When cement slurry come out on surface that’s call laitance. It is prevented by following steps
nikeetasharma
Laitance can be reduced by controlling the amount of water in the concrete mix during construction. If too much water remains in the concrete than various other issues can be found like greater shrinkage with the possibility of more cracks and reduced compressive strength overall.